Home Stainless Steel Circle Rings Stainless Steel 310S Circle Rings

Stainless Steel 310S Circle Rings

Stainless Steel 310S Circle RIngs

A reputable business with a focus on the supply of premium Stainless Steel 310S Circle Rings is Shree Viratra Enterprises. The austenitic stainless steel 310S is renowned for its outstanding corrosion resistance, excellent oxidation resistance, and superb high-temperature strength in a variety of settings.
The top-quality stainless steel 310S material used to create the stainless steel 310S circle rings produced by Shree Viratra Enterprises normally has the following components:
Chromium (Cr): The 24% to 26% of chromium in stainless steel 310S offers exceptional resistance to corrosion, oxidation, and scaling at high temperatures.
Nickel (Ni): The typical nickel content of stainless steel 310S is between 19% and 22%, which improves the material’s corrosion resistance and contributes to its strength and ductility at high temperatures. Carbon (C): The maximum carbon content of stainless steel 310S is typically 0.08%. Because there is less carbon in the material, there is less of a chance that welding may cause sensitization, which can cause corrosion problems.
The range of 2% to 2.5% manganese (Mn) in stainless steel 310S contributes to the material’s mechanical characteristics and workability.
Stainless Steel 310S commonly contains silicon in the range of 1.0% to 1.5%, which contributes to the material’s improved resistance to scaling at high temperatures.
Other Elements: minute amounts of other elements, such as nitrogen (N), phosphorus (P), and sulphur (S), may also be present in stainless steel 310S. These other elements are typically present in very minute proportions and are controlled within predetermined ranges.

310S Stainless Steel Circle Rings Specifications

Specifications:ASTM A240 / ASME SA240
Dimensions:ASTM, ASME and API
Thickness:1 Mm To 100 Mm
Diameter:Upto 2000 Mm
Circle Diameter:3″ DIA up to 38″ DIA 1500 lbs max
Ring Diameter:3″ OD up to 48″ OD Up to 900 lbs max

310S Stainless Steel Circle Rings Equivalent Grades

STANDARD UNS WERKSTOFF NR. AFNOR EN JIS BS GOST
SS 310S
S31008
1.4845
-
-
-
-
-

310S Stainless Steel Circle Rings Chemical Composition

Grade C Mn Si P S Cr Mo Ni N
SS 310S
0.08 max
2.00 max
1.50 max
0.045 max
0.030 max
26.0 max
-
22.0
-

Mechanical Properties of 310S Stainless Steel Circle Rings

Grade Tensile Strength (MPa) min Yield Strength 0.2% Proof (MPa) min Elongation (% in 50mm) min Hardness Rockwell B (HR B) max Hardness Brinell (HB) max
SS 310S
515
205
40
95
217