Stainless Steel 316H Circle Rings

Stainless Steel 316H Circle RIngs

A reputable business with a solid reputation for offering Stainless Steel 316H Circle Rings is Shree Viratra Enterprises. A high-carbon version of stainless steel 316, known as stainless steel 316H, was created with the goal of improving high-temperature strength and resistance to sensitization.
The premium-grade stainless steel 316H material used to create the stainless steel 316H circle rings produced by Shree Viratra Enterprises normally comprises of the following components:
Chromium (Cr): Stainless Steel 316H has a chromium content of between 16% and 18%, which offers high corrosion resistance, including resistance to oxidation and a number of other corrosive agents.
Nickel (Ni): Stainless Steel 316H commonly contains 10% to 14% nickel, which improves the substance’s ductility, mechanical characteristics, and resistance to corrosion. Molybdenum (Mo): The amount of molybdenum in stainless steel 316H ranges from 2% to 3%, greatly enhancing the material’s resistance to pitting and crevice corrosion, particularly in chloride-containing environments.
Carbon (C): The carbon content of stainless steel 316H is typically between 0.04% and 0.10% higher than that of normal stainless steel 316. The material’s high-temperature strength and creep resistance are enhanced by the added carbon.
Manganese (Mn): Stainless Steel 316H contains 2% to 2.5% manganese, which helps to enhance the material’s mechanical characteristics and workability.
Silicon (Si): Stainless Steel 316H normally has silicon content in the range of 0.75 to 1 percent, which improves the substance’s resistance to scaling at high temperatures.
Other Elements: Trace amounts of other elements, such as nitrogen (N), may also be present in stainless steel 316H.

316H Stainless Steel Circle Rings Specifications

Specifications:ASTM A240 / ASME SA240
Dimensions:ASTM, ASME and API
Thickness:1 Mm To 100 Mm
Diameter:Upto 2000 Mm
Circle Diameter:3″ DIA up to 38″ DIA 1500 lbs max
Ring Diameter:3″ OD up to 48″ OD Up to 900 lbs max

316H Stainless Steel Circle Rings Equivalent Grades

STANDARD UNS WERKSTOFF NR. AFNOR EN JIS BS GOST
SS 316H
S31609
1.4919
-
-
-
-
-

316H Stainless Steel Circle Rings Chemical Composition

Grade C Mn Si P S Cr Mo Ni N
SS 316H
0.10 max
0.10 max
0.75 max
0.045 max
0.03 max
18.0
3.00
14.0
-

Mechanical Properties of 316H Stainless Steel Circle Rings

Grade Tensile Strength (MPa) min Yield Strength 0.2% Proof (MPa) min Elongation (% in 50mm) min Hardness Rockwell B (HR B) max Hardness Brinell (HB) max
SS 316H
8.0 g/cm3
1400 °C (2550 °F)
Psi – 75,000 , MPa – 515
Psi – 30,000 , MPa – 205
35 %