Stainless Steel 304L Sheets, Plates & Coils

Stainless Steel 304L Sheets Plates Coils

Shree Viratra Enterprises is one of India’s leading manufacturers of premium Stainless Steel 304L Sheets, Plates, and Coils used in numerous industries. These stainless steel 304L plates are also produced and machined to meet the plumbing needs of our clients. Stainless steel 304L coils perform exceptionally well at low temperatures and adapt well to cold working. Since SS 304L Sheets have good welding characteristics, post-weld annealing is typically not required for performance restoration. SS 304L Welded Plates offer excellent corrosion resistance in a variety of conditions. We offer a wide range of sizes and shapes of premium SS 304L Sheets made from raw materials that satisfy both domestic and international quality standards.

Specification of Stainless Steel 304L Sheets, Plates, Coils

Specifications : ASTM A240 / ASME SA240

Dimensions : ASTM, ASME, and API

Width 1000mm, 1219mm, 1500mm, 1800mm, 2000mm, 2500mm, 3000mm, 3500mm, etc

Thickness: 4mm-100mm

Length : 2000mm, 2440mm, 3000mm, 5800mm, 6000mm, etc

Surface Finish : 2B, 2D, BA, NO.1, NO.4, NO.8, 8K, mirror, chequered, embossed, hairline, sand blast, Brush, etching, Hot rolled plate (HR), Cold rolled sheet (CR), SATIN (Met with Plastic Coated) etc

Hardness : Soft, Hard, Half Hard, Quarter Hard, Spring Hard etc.

Form : Coils, Foils, Rolls, Plain Sheet, Shim Sheet, Perforated Sheet, Chequered Plate, Strip, Flats, Blank (Circle), Ring (Flange) etc.

Equivalent Grades of Stainless Steel 304L Sheets, Plates and Coils

STANDARD UNS WERKSTOFF NR. AFNOR EN JIS BS GOST
SS 304L
S30403
1.4306 / 1.4307
Z3CN18-10
X2CrNi18-9 / X2CrNi19-11
SUS 304L
3304S11
03Х18Н11

Chemical Composition of Stainless Steel 304L Sheets and Plates, Coils

Grade C Mn Si P S Cr Mo Ni N
SS 304L
0.035 max
2.0 max
1.0 max
0.045 max
0.03 max
18 – 20
-
8 – 13
-

Stainless Steel 304L Sheets, Plate, Coils Mechanical Properties

Density Melting Point Tensile Strength Yield Strength (0.2%Offset) Elongation
8.0 g/cm3
1400 °C (2550 °F)
Psi – 75000 , MPa – 515
Psi – 30000 , MPa – 205
35 %